Product Specifications

Material	Aluminum Alloy 6005A
Process	Forging + CNC + Heat Treatment
Surface Treatment	Anodizing, Hard Anodizing, Powder Coating, Sandblasting, Laser Carving, Silk Screening, Plating, Black Oxide, Polishing
Manufacturing Capability	Customized based on product complexity and quantities
Experience	12 Years Aluminum Machining Service
Packaging	Standard Export Wooden Pallets or Custom Options
MOQ	1 piece
Lead Time	Mold: 15-20 Days, Process: 15-20 Days

Chemical Composition of 6005A Aluminum Alloy

Element	Content (%)
Si (Silicon)	0.5-0.9
Fe (Iron)	0.35 max
Cu (Copper)	0.3 max
Mn (Manganese)	0.5 max
Mg (Magnesium)	0.4-0.7
Cr (Chromium)	0.3 max
Zn (Zinc)	0.2 max
Ti (Titanium)	0.1 max
Al (Aluminum)	Remainder

Technical Properties

Property	Value
Density	2.70 g/cc
Tensile Strength, Ultimate	260 MPa
Tensile Strength, Yield	240 MPa
Elongation at Break	8.0%
Modulus of Elasticity	69.0 GPa
Hardness, Brinell	95
Thermal Conductivity	189 W/m-K
Electrical Resistivity	0.00000349 ohm-cm @ 20°C
Melting Point	607.2 - 654°C

Product Showcase

Tags:

Forged Metal Parts,

Forged Metal Components,

Metal Forgings

Orbital Aluminum Forgings Orbital Brake Lever Corrosion Resistant

Contact Now

6061 Aluminum Forged Parts For New Energy Vehicles

Contact Now

Anti Corrosion Track Fasteners Aluminum Forgings for Outlast Extreme Environments

Contact Now

Train 6005A-T6 Aluminum Alloy Forged Components Lightweight

Contact Now

High Precision Aluminum Forgings Linear Motors For Mechanical Engineering

Contact Now

Aerospace Grade 7049 Aluminium Forgings Billet T73 Temper Anti Corrosion

Contact Now

2618 T6 Aluminum Forgings Anti Corrosion For Turbine Blades

Contact Now

PRODUCTS DETAILS

Products

Forged Components

Aluminum Forgings

Titanium Forgings

Stainless Steel Forgings

Copper Forgings

Forged Metal Rings

Forged Rings

Waterjet Cutting Services

Aluminum Forged Rings

Titanium Forged Rings

Air Disc Brake Core Components

Precision CNC Components

Splined Shaft

6005A Aluminum Metal Par For High Speed Train Carriage / Transportation OEM Forging Parts

MOQ:	1PCS
Price:	Negotiations
Standard Packaging:	wooden pallet
Delivery Period:	15~30days
Payment Method:	T/T, L/C
Supply Capacity:	10000pcs /per month

Detail Information

Product Description

Detail Information

Place of Origin

CHINA

Brand Name

JIMA

Certification

ISO9001-2008,SGS,ROHS.

Model Number

ALP

Application:

Military,Marine

Name:

OEM 6005A Forging Aluminum Parts For High Speed Train Carriage / Transportation Parts/Forging Aluminum/ Forging Parts

Standard:

JIS, DIN, BS, ASTM, SAE.

Alloy:

6005A

Surface Treatment:

Anodizing,Plating,Satin,Painting,Powder Coating,Anodized Etc

Process:

Forging/Forged

Mold:

Can Be Customized

Sample:

Can Be Customized

Minimum Order Quantity:

1PCS

Price:

Negotiations

Packaging Details:

wooden pallet

Delivery Time:

15~30days

Payment Terms:

T/T, L/C

Supply Ability:

10000pcs /per month

Highlight

6005A Forging Aluminum Parts

Transportation Aluminum Metal Parts OEM

Train Carriage Forging Aluminum Parts

Product Description

6005A Aluminum Metal Parts for High-Speed Train Carriage

OEM Forging Aluminum Parts for Transportation Applications

Our Manufacturing Advantages

3 technical patents and 2 practical patents for high-silicon aluminum alloy processing
Multiple professional presses optimized for high-silicon aluminum alloy deformation
Intermediate frequency heating furnaces for weak magnetic materials
Advanced forging processes for pistons and swash plates
University research partnerships for technical innovation
Certified high-tech enterprise
Development capabilities: aluminum, titanium, super alloy, and non-ferrous metal forging

Product Specifications

Material	Aluminum Alloy 6005A
Process	Forging + CNC + Heat Treatment
Surface Treatment	Anodizing, Hard Anodizing, Powder Coating, Sandblasting, Laser Carving, Silk Screening, Plating, Black Oxide, Polishing
Manufacturing Capability	Customized based on product complexity and quantities
Experience	12 Years Aluminum Machining Service
Packaging	Standard Export Wooden Pallets or Custom Options
MOQ	1 piece
Lead Time	Mold: 15-20 Days, Process: 15-20 Days

Chemical Composition of 6005A Aluminum Alloy

Element	Content (%)
Si (Silicon)	0.5-0.9
Fe (Iron)	0.35 max
Cu (Copper)	0.3 max
Mn (Manganese)	0.5 max
Mg (Magnesium)	0.4-0.7
Cr (Chromium)	0.3 max
Zn (Zinc)	0.2 max
Ti (Titanium)	0.1 max
Al (Aluminum)	Remainder

Technical Properties

Property	Value
Density	2.70 g/cc
Tensile Strength, Ultimate	260 MPa
Tensile Strength, Yield	240 MPa
Elongation at Break	8.0%
Modulus of Elasticity	69.0 GPa
Hardness, Brinell	95
Thermal Conductivity	189 W/m-K
Electrical Resistivity	0.00000349 ohm-cm @ 20°C
Melting Point	607.2 - 654°C