MOQ:	1PCS
Price:	Negotiations
Standard Packaging:	Standard Export Wooden Pallet
Delivery Period:	15~30days
Payment Method:	T/T, L/C
Supply Capacity:	10000 pcs /per month

Details Information

Product Description

Detail Information

Place of Origin

CHINA

Brand Name

JIMA

Certification

ISO9001-2008,SGS,ROHS.

Model Number

ALP

Application:

Automotive/Railway/Aerospace

Name:

OEM 7079 Forging Aluminum Parts For Skeleton Large Forgings/ Spare Parts/Die Forged

Standard:

JIS, DIN, BS, ASTM, SAE.

Alloy:

7079

Surface Treatment:

Anodizing,Plating,Satin,Painting,Powder Coating,Anodized Etc

Process:

Forging/Forged

Mold:

Can Be Customized

Sample:

Can Be Customized

Highlight:

OEM 7079 Forging Aluminum Parts

Skeleton Forging Aluminum Parts

7079 Forged Aluminum Metal Parts

Product Description

OEM 7079 Forging Aluminum Parts For Skeleton Large Forgings/Spare Parts/Die Forged

Product Details

Material	Aluminum Alloy 7079
Process	Forging+CNC+Heat Treatment
Surface Treatment	Transparent, Color Anodized, Hard Anodizing, Powder Coating; Sandblasting, Laser Carving, Silk Screening; Nickel-Plated, Chrome, Galvanized, Silver/Gold Plating; Black Oxide Coating, Polishing; etc...
Manufacture Ability	Depends on The Complexity Of Different Products And Quantities
Experience	Aluminum Machining Service for 12 Years
Packaging	Standard Export Wooden Pallets Another Request According to Your Needs
MOQ	1pcs
Sample	Can Be Customized
Mold	Can Be Customized
Lead Time	Mold for 15-20 Days Process for 15-20 Days
OEM	Can Be Customized

Chemical Composition of 7079

Alloy

Others

Each

Total

7079

0.30max

0.40max

0.40-0.80

0.10-0.30

2.90-3.70

0.10-0.25

3.80-4.80

0.10max

0.05max

0.15max

Rest

Technical Specifications of 7079

7079 Aluminum Mechanical Properties

Hardness, Brinell	150	150	AA; Typical; 500 g load; 10 mm ball
Hardness, Knoop	191	191	Converted from Brinell Hardness Value
Hardness, Rockwell A	53.5	53.5	Converted from Brinell Hardness Value
Hardness, Rockwell B	87	87	Converted from Brinell Hardness Value
Hardness, Vickers	175	175	Converted from Brinell Hardness Value
Ultimate Tensile Strength	572 MPa	83000 psi	AA; Typical
Tensile Yield Strength	503 MPa	73000 psi	AA; Typical
Elongation at Break	11 %	11 %	AA; Typical; 1/16 in. (1.6 mm) Thickness
Elongation at Break	11 %	11 %	AA; Typical; 1/2 in. (12.7 mm) Diameter
Modulus of Elasticity	71.7 GPa	10400 ksi	AA; Typical; Average of tension and compression. The compression modulus is about 2% greater than tensile modulus.
Poisson’s Ratio	0.33	0.33
Fatigue Strength	159 MPa	23000 psi	AA; 500,000,000 cycles completely reversed stress; RR Moore machine/specimen
Fracture Toughness	20 MPa-m½	18.2 ksi-in½	K(IC) in S-L Direction
Fracture Toughness	25 MPa-m½	22.8 ksi-in½	K(IC) in T-L Direction
Fracture Toughness	29 MPa-m½	26.4 ksi-in½	K(IC) in L-T Direction
Machinability	70 %	70 %	0-100 Scale of Aluminum Alloys
Shear Modulus	26.9 GPa	3900 ksi
Shear Strength	331 MPa	48000 psi	AA; Typical

7079 Aluminum Thermal Properties

CTE, linear 68°F	23.6 µm/m-°C	13.1 µin/in-°F	AA; Typical; Average over 68-212°F range.
CTE, linear 250°C	25.2 µm/m-°C	14 µin/in-°F	Average over the range 20-300ºC
Specific Heat Capacity	0.96 J/g-°C	0.229 BTU/lb-°F
Thermal Conductivity	130 W/m-K	900 BTU-in/hr-ft²-°F	AA; Typical at 77°F
Melting Point	477 – 635 °C	890 – 1175 °F	AA; Typical range based on typical composition for wrought products 1/4 inch thickness or more significant. Homogenization may raise the eutectic melting temperature by 20-40°F but usually does not eliminate eutectic melting.
Solidus	477 °C	890 °F	AA; Typical
Liquidus	635 °C	1175 °F	AA; Typical

Product Show

OEM 7079 Forging Aluminum Parts For Skeleton Large Die Forged Spare Parts 0

OEM 7079 Forging Aluminum Parts For Skeleton Large Die Forged Spare Parts 1

Tags:

Forged Metal Parts,

Forged Metal Components,

Metal Forgings

Orbital Aluminum Forgings Orbital Brake Lever Corrosion Resistant

Contact Now

6061 Aluminum Forged Parts For New Energy Vehicles

Contact Now

Anti Corrosion Track Fasteners Aluminum Forgings for Outlast Extreme Environments

Contact Now

Train 6005A-T6 Aluminum Alloy Forged Components Lightweight

Contact Now

High Precision Aluminum Forgings Linear Motors For Mechanical Engineering

Contact Now

Aerospace Grade 7049 Aluminium Forgings Billet T73 Temper Anti Corrosion

Contact Now

2618 T6 Aluminum Forgings Anti Corrosion For Turbine Blades

Contact Now

Hard 7050 Aluminum Alloy AlZn6CuMnZr A97050 , Forging 7050 T6 Aluminum Billet

Contact Now

Temper T6 5456 Aluminum Forgings Billet AlMg5Mn1 EN AW 5456A/AlMg5Mn

Contact Now

Skeleton Forging 7079 Aluminium Alloy Billet High Purity 7000 Series

Contact Now

Airplane 7075 T6 Billet Aluminum Forgings , Super Duralumin Aluminium Alloy 7075

Contact Now

PRODUCTS DETAILS

Products

Forged Components

Aluminum Forgings

Titanium Forgings

Stainless Steel Forgings

Magnesium Forgings

Copper Forgings

Forged Metal Rings

Forged Rings

Waterjet Cutting Services

Aluminum Forged Rings

Titanium Forged Rings

Air Disc Brake Core Components

Precision CNC Components

Splined Shaft

OEM 7079 Forging Aluminum Parts For Skeleton Large Die Forged Spare Parts

MOQ:	1PCS
Price:	Negotiations
Standard Packaging:	Standard Export Wooden Pallet
Delivery Period:	15~30days
Payment Method:	T/T, L/C
Supply Capacity:	10000 pcs /per month

Detail Information

Product Description

Detail Information

Place of Origin

CHINA

Brand Name

JIMA

Certification

ISO9001-2008,SGS,ROHS.

Model Number

ALP

Application:

Automotive/Railway/Aerospace

Name:

OEM 7079 Forging Aluminum Parts For Skeleton Large Forgings/ Spare Parts/Die Forged

Standard:

JIS, DIN, BS, ASTM, SAE.

Alloy:

7079

Surface Treatment:

Anodizing,Plating,Satin,Painting,Powder Coating,Anodized Etc

Process:

Forging/Forged

Mold:

Can Be Customized

Sample:

Can Be Customized

Minimum Order Quantity:

1PCS

Price:

Negotiations

Packaging Details:

Standard Export Wooden Pallet

Delivery Time:

15~30days

Payment Terms:

T/T, L/C

Supply Ability:

10000 pcs /per month

Highlight

OEM 7079 Forging Aluminum Parts

Skeleton Forging Aluminum Parts

7079 Forged Aluminum Metal Parts

Product Description

OEM 7079 Forging Aluminum Parts For Skeleton Large Forgings/Spare Parts/Die Forged

Product Details

Material	Aluminum Alloy 7079
Process	Forging+CNC+Heat Treatment
Surface Treatment	Transparent, Color Anodized, Hard Anodizing, Powder Coating; Sandblasting, Laser Carving, Silk Screening; Nickel-Plated, Chrome, Galvanized, Silver/Gold Plating; Black Oxide Coating, Polishing; etc...
Manufacture Ability	Depends on The Complexity Of Different Products And Quantities
Experience	Aluminum Machining Service for 12 Years
Packaging	Standard Export Wooden Pallets Another Request According to Your Needs
MOQ	1pcs
Sample	Can Be Customized
Mold	Can Be Customized
Lead Time	Mold for 15-20 Days Process for 15-20 Days
OEM	Can Be Customized

Chemical Composition of 7079

Alloy

Others

Each

Total

7079

0.30max

0.40max

0.40-0.80

0.10-0.30

2.90-3.70

0.10-0.25

3.80-4.80

0.10max

0.05max

0.15max

Rest

Technical Specifications of 7079

7079 Aluminum Mechanical Properties

Hardness, Brinell	150	150	AA; Typical; 500 g load; 10 mm ball
Hardness, Knoop	191	191	Converted from Brinell Hardness Value
Hardness, Rockwell A	53.5	53.5	Converted from Brinell Hardness Value
Hardness, Rockwell B	87	87	Converted from Brinell Hardness Value
Hardness, Vickers	175	175	Converted from Brinell Hardness Value
Ultimate Tensile Strength	572 MPa	83000 psi	AA; Typical
Tensile Yield Strength	503 MPa	73000 psi	AA; Typical
Elongation at Break	11 %	11 %	AA; Typical; 1/16 in. (1.6 mm) Thickness
Elongation at Break	11 %	11 %	AA; Typical; 1/2 in. (12.7 mm) Diameter
Modulus of Elasticity	71.7 GPa	10400 ksi	AA; Typical; Average of tension and compression. The compression modulus is about 2% greater than tensile modulus.
Poisson’s Ratio	0.33	0.33
Fatigue Strength	159 MPa	23000 psi	AA; 500,000,000 cycles completely reversed stress; RR Moore machine/specimen
Fracture Toughness	20 MPa-m½	18.2 ksi-in½	K(IC) in S-L Direction
Fracture Toughness	25 MPa-m½	22.8 ksi-in½	K(IC) in T-L Direction
Fracture Toughness	29 MPa-m½	26.4 ksi-in½	K(IC) in L-T Direction
Machinability	70 %	70 %	0-100 Scale of Aluminum Alloys
Shear Modulus	26.9 GPa	3900 ksi
Shear Strength	331 MPa	48000 psi	AA; Typical

7079 Aluminum Thermal Properties

CTE, linear 68°F	23.6 µm/m-°C	13.1 µin/in-°F	AA; Typical; Average over 68-212°F range.
CTE, linear 250°C	25.2 µm/m-°C	14 µin/in-°F	Average over the range 20-300ºC
Specific Heat Capacity	0.96 J/g-°C	0.229 BTU/lb-°F
Thermal Conductivity	130 W/m-K	900 BTU-in/hr-ft²-°F	AA; Typical at 77°F
Melting Point	477 – 635 °C	890 – 1175 °F	AA; Typical range based on typical composition for wrought products 1/4 inch thickness or more significant. Homogenization may raise the eutectic melting temperature by 20-40°F but usually does not eliminate eutectic melting.
Solidus	477 °C	890 °F	AA; Typical
Liquidus	635 °C	1175 °F	AA; Typical

Product Show

OEM 7079 Forging Aluminum Parts For Skeleton Large Die Forged Spare Parts 0

OEM 7079 Forging Aluminum Parts For Skeleton Large Die Forged Spare Parts 1

Tags: